Atomic layer deposition and properties of mixed Ta2O5 and ZrO2 films

Näytä kaikki kuvailutiedot



Pysyväisosoite

http://hdl.handle.net/10138/179111

Lähdeviite

Kukli , K , Kemell , M , Vehkamäki , M , Heikkilä , M J , Mizohata , K , Kalam , K , Ritala , M , Leskelä , M , Kundrata , I & Frohlich , K 2017 , ' Atomic layer deposition and properties of mixed Ta2O5 and ZrO2 films ' , AIP Advances , vol. 7 , no. 2 , 025001 . https://doi.org/10.1063/1.4975928

Julkaisun nimi: Atomic layer deposition and properties of mixed Ta2O5 and ZrO2 films
Tekijä: Kukli, Kaupo; Kemell, Marianna; Vehkamäki, Marko; Heikkilä, Mikko J.; Mizohata, Kenichiro; Kalam, Kristjan; Ritala, Mikko; Leskelä, Markku; Kundrata, Ivan; Frohlich, Karol
Tekijän organisaatio: Department of Chemistry
Department of Physics
Mikko Ritala / Principal Investigator
Päiväys: 2017-02
Kieli: eng
Sivumäärä: 15
Kuuluu julkaisusarjaan: AIP Advances
ISSN: 2158-3226
DOI-tunniste: https://doi.org/10.1063/1.4975928
URI: http://hdl.handle.net/10138/179111
Tiivistelmä: Thin solid films consisting of ZrO2 and Ta2O5 were grown by atomic layer deposition at 300 degrees C. Ta2O5 films doped with ZrO2, TaZr2.75O8 ternary phase, or ZrO2 doped with Ta2O5 were grown to thickness and composition depending on the number and ratio of alternating ZrO2 and Ta2O5 deposition cycles. All the films grown exhibited resistive switching characteristics between TiN and Pt electrodes, expressed by repetitive current-voltage loops. The most reliable windows between high and low resistive states were observed in Ta2O5 films mixed with relatively low amounts of ZrO2, providing Zr to Ta cation ratio of 0.2. (C) 2017 Author(s).
Avainsanat: OXIDE THIN-FILMS
RESISTIVE SWITCHING MEMORIES
INSULATOR-METAL STRUCTURES
TANTALUM OXIDE
ORTHORHOMBIC ZIRCONIA
DIELECTRIC-PROPERTIES
TETRAGONAL ZIRCONIA
RESISTANCE
INTERFACE
EPITAXY
114 Physical sciences
116 Chemical sciences
Vertaisarvioitu: Kyllä
Tekijänoikeustiedot: cc_by
Pääsyrajoitteet: openAccess
Rinnakkaistallennettu versio: publishedVersion


Tiedostot

Latausmäärä yhteensä: Ladataan...

Tiedosto(t) Koko Formaatti Näytä
1_2E4975928.pdf 10.83MB PDF Avaa tiedosto

Viite kuuluu kokoelmiin:

Näytä kaikki kuvailutiedot