Synthesis and solution properties of block polyampholyte

Show full item record



Permalink

http://urn.fi/URN:NBN:fi:hulib-202002281427
Title: Synthesis and solution properties of block polyampholyte
Author: Meriläinen, Kati
Contributor: University of Helsinki, Faculty of Science
Publisher: Helsingin yliopisto
Date: 2020
Language: eng
URI: http://urn.fi/URN:NBN:fi:hulib-202002281427
http://hdl.handle.net/10138/312506
Thesis level: master's thesis
Degree program: Materiaalitutkimuksen maisteriohjelma
Master's Programme in Materials Research
Magisterprogrammet i materialforskning
Specialisation: Polymeerimateriaalien kemia
Polymer Materials Chemistry
Polymermaterialkemi
Discipline: none
Abstract: In this thesis, synthesis and solution properties of the polyampholyte poly(acrylic acid)-b-poly[(vinylbenzyl)trimethylammonium chloride], PAA-PVBTMA-Cl, were investigated in aqueous solutions. First, the diblock copolymer was synthesized via RAFT polymerization where poly(acrylic acid), PAA was used as a chain transfer agent (CTA). In addition, the homopolymer poly[(vinylbenzyl)trimethylammonium chloride], PVBTMA-Cl, was synthesized via RAFT polymerization to compare the solution properties with the block copolymer. Molar masses of the polymers were determined using several methods such as NMR, UV-Vis spectroscopy and SEC. The experimental molar masses were close to theoretical values and block ratio in diblock copolymer from NMR was 30% of AA and 70% of VBTMA-Cl. Furthermore, the solution properties of the polyampholyte were studied under external stimuli such as pH and temperature. UCST type of behaviour was observed for aqueous PAA-PVBTMA-Cl solutions when the hydrophobic trifluoromethanesulfonate (OTf) anion was introduced. In addition, self-assembly of the diblock copolymer was confirmed by zeta potential measurements in different pH conditions. The expected reverse of the micelle structure with changing pH was not observed. However, aqueous PAA-PVBTMA-Cl showed UCST behaviour and micellization induced by the hydrophobic counterion.


Files in this item

Total number of downloads: Loading...

Files Size Format View
Merilainen_Kati_Pro_gradu_2020.pdf 1.542Mb PDF View/Open

This item appears in the following Collection(s)

Show full item record