Understanding the Stabilizing Effects of Nanoscale Metal Oxide and Li–Metal Oxide Coatings on Lithium-Ion Battery Positive Electrode Materials

Näytä kaikki kuvailutiedot



Pysyväisosoite

http://hdl.handle.net/10138/334428

Lähdeviite

Ahaliabadeh , Z , Miikkulainen , V , Mäntymäki , M , Mousavihashemi , S , Lahtinen , J , Lide , Y , Jiang , H , Mizohata , K , Kankaanpää , T & Kallio , T 2021 , ' Understanding the Stabilizing Effects of Nanoscale Metal Oxide and Li–Metal Oxide Coatings on Lithium-Ion Battery Positive Electrode Materials ' , ACS Applied Materials & Interfaces , vol. 13 , no. 36 , pp. 42773-42790 . https://doi.org/10.1021/acsami.1c11165

Julkaisun nimi: Understanding the Stabilizing Effects of Nanoscale Metal Oxide and Li–Metal Oxide Coatings on Lithium-Ion Battery Positive Electrode Materials
Tekijä: Ahaliabadeh, Zahra; Miikkulainen, Ville; Mäntymäki, Miia; Mousavihashemi, Seyedabolfazl; Lahtinen, Jouko; Lide, Yao; Jiang, Hua; Mizohata, Kenichiro; Kankaanpää, Timo; Kallio, Tanja
Tekijän organisaatio: Department of Chemistry
Materials Physics
Päiväys: 2021-09-15
Kieli: eng
Sivumäärä: 18
Kuuluu julkaisusarjaan: ACS Applied Materials & Interfaces
ISSN: 1944-8244
DOI-tunniste: https://doi.org/10.1021/acsami.1c11165
URI: http://hdl.handle.net/10138/334428
Tiivistelmä: Nickel-rich layered oxides, such as LiNi0.6Co0.2Mn0.2O2 (NMC622), are high-capacity electrode materials for lithium-ion batteries. However, this material faces issues, such as poor durability at high cut-off voltages (>4.4 V vs Li/Li+), which mainly originate from an unstable electrode-electrolyte interface. To reduce the side reactions at the interfacial zone and increase the structural stability of the NMC622 materials, nanoscale (
Avainsanat: 116 Chemical sciences
Lithium-ion battery
ALD
electrode coating
titanium oxide
lithium titanate
Ni-rich positive electrode
ATOMIC LAYER DEPOSITION
ENHANCED ELECTROCHEMICAL PERFORMANCE
CATHODE MATERIALS
RICH
SURFACE
NICKEL
LINI0.8CO0.1MN0.1O2
AL2O3
NANOPARTICLES
DEGRADATION
Vertaisarvioitu: Kyllä
Tekijänoikeustiedot: cc_by
Pääsyrajoitteet: openAccess
Rinnakkaistallennettu versio: publishedVersion


Tiedostot

Latausmäärä yhteensä: Ladataan...

Tiedosto(t) Koko Formaatti Näytä
acsami.1c11165.pdf 8.219MB PDF Avaa tiedosto

Viite kuuluu kokoelmiin:

Näytä kaikki kuvailutiedot