Determining the Stiffness of Ex Vivo Porcine Lenses

Show full item record



Permalink

http://urn.fi/URN:NBN:fi-fe201903229784
Title: Determining the Stiffness of Ex Vivo Porcine Lenses
Author: Sillanpää, Tom
Contributor: University of Helsinki, Faculty of Science
Publisher: Helsingin yliopisto
Date: 2019
Language: eng
URI: http://urn.fi/URN:NBN:fi-fe201903229784
http://hdl.handle.net/10138/300345
Thesis level: master's thesis
Discipline: Fysiikka
Abstract: Linear elastic properties of ex vivo porcine lenses were characterized by compression and indentation tests. Compression tests were performed on un-glued lenses (N = 76), the average stiffness 12 ± 3 kPa (± sigma) and thickness 7.0 ± 0.3 mm were measured at 24 - 30 hours post mortem. For glued lenses (N = 70), the average stiffness was 15 ± 4 kPa and thickness 7.2 ± 0.4 mm. The shear modulus was 1.5 ± 0.3 kPa (N = 10) on average measured at 12 hours post mortem with indentation test. Compared to intact lenses, decapsulated lenses were 41% less stiff (N = 5) as measured with the compression test and the shear modulus was 65 % less (N = 10) as determined by indentation.Sian linssien lineaarisia kimmoisuusominaisuuksia karakterisoitiin ex vivo kahdella menetelmällä: puristus- ja indentaatiotestillä. Puristustestin tuloksena saatin ei-liimattujen linssien (N = 76) osalta jäykkyydeksi 12 ± 3 kPa (± sigma) ja paksuudeksi 7.0 ± 0.3 mm, mitattuna aika välillä 24-30 h post mortem. Linssit, jotka olivat liimattuina, olivat jäykkyydeltään 15 ± 4 kPa ja paksuudeltaan 7.2 ± 0.4 mm. Indentaatiotestien avulla määritetty leikkausmoduulin arvo oli keskimäärin 1.5 ± 0.3 kPa (N = 10) mitattuna noin 12 h post mortem. Linssiä ympäröivän jäykemmän kuorikalvon poistaminen johti jäykkyyden vähentymiseen 41 % sekä leikkausmoduulin pienetymiseen 65 %.


Files in this item

Files Size Format View

There are no files associated with this item.

This item appears in the following Collection(s)

Show full item record